S-Plastics Thermocomp DF0069P resin is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features
of this material include: Exceptional Processing.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 137 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.7 | % | ASTM D 638 |
| Flexural Stress | 210 | MPa | ASTM D 790 |
| Flexural Modulus | 9030 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 801 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 128 | J/m | ASTM D 256 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.46 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 | % | ASTM D 955 |
| Source GMD, last updated:09/27/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/27/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp DF0069P.pdf |
|