S-Plastics Thermocomp R1000HI620 resin is Impact modified Polyamide 66 injection moulding resin.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1900 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 72 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1900 | MPa | ISO 178 |
| Hardness, Rockwell R | 112 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 80 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -20°C | 65 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 55 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 80 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 65 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | >100 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | >100 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.2E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 192 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 190 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 220 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 72 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 1 - 1.2 | % | S-Plastics Method |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 5.5 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 1.5 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+16 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+16 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 2.9 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.0067 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.015 | - | IEC 60250 |
| Comparative Tracking Index | 550 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 0.75 | mm | UL 94 |
| UL Recognized, 94HB Flame Class Rating 2nd value (3) | 3 | mm | UL 94 |
| FMVSS Burning Speed, thickness 2 mm | 15 | mm/min | FMVSS 302 |
| Source GMD, last updated:11/04/2003 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 75 - 85 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.2 | % |
| Melt Temperature | 260 - 280 | °C |
| Nozzle Temperature | 250 - 270 | °C |
| Front - Zone 3 Temperature | 260 - 280 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Rear - Zone 1 Temperature | 260 - 280 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 70 - 90 | °C |
| Source GMD, last updated:11/04/2003 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |