S-Plastics Thermocomp EX06430H resin is a compound based on Polyimide resin containing Proprietary Filler(s).
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 110 | MPa | ASTM D 638 |
| Tensile Stress, break | 90 | MPa | ASTM D 638 |
| Tensile Strain, yield | 6.7 | % | ASTM D 638 |
| Tensile Strain, break | 13.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3660 | MPa | ASTM D 638 |
| Flexural Modulus | 3660 | MPa | ASTM D 790 |
| Tensile Stress, yield | 106 | MPa | ISO 527 |
| Tensile Stress, break | 90 | MPa | ISO 527 |
| Tensile Strain, yield | 6 | % | ISO 527 |
| Tensile Strain, break | 10.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3500 | MPa | ISO 527 |
| Flexural Stress | 133 | MPa | ISO 178 |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1383 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 48 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 10 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 73 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 195 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 194 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.34 - 1.4 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.7 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.8 | % | ASTM D 955 |
| Source GMD, last updated:08/02/2007 | |||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |