S-Plastics Thermocomp ZX06323 resin is This material is mineral filled PPO grade with high dielectric constant and low loss tangent
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 0 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 54 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4.2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4140 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 102 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 102 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3940 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 0 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 54 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 4.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4080 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 4390 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 294 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 46 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 122 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.95 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.1 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.64 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.56 | % | ASTM D 955 |
| Density | 1.95 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 8 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Dissipation Factor, 900MHz | 0.003 | - | ASTM D 150 |
| Relative Permittivity, 900MHz | 6.4 | - | ASTM D 2520 - Mth B |
| Source GMD, last updated:2007/06/28 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 105 | °C |
| Drying Time | 3 - 5 | hrs |
| Melt Temperature | 295 - 305 | °C |
| Nozzle Temperature | 290 - 295 | °C |
| Front - Zone 3 Temperature | 300 - 305 | °C |
| Middle - Zone 2 Temperature | 290 - 295 | °C |
| Rear - Zone 1 Temperature | 280 - 285 | °C |
| Mold Temperature | 90 | °C |
| Back Pressure | 9 | MPa |
| Screw Speed | 100 | rpm |
| Source GMD, last updated:2007/06/28 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp ZX06323.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|