S-Plastics Thermocomp RF007SXQ resin is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include:
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 195 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.9 | % | ASTM D 638 |
| Flexural Stress | 297 | MPa | ASTM D 790 |
| Flexural Modulus | 10680 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1228 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 106 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 250 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.42 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.4 | % | ASTM D 955 |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||