S-Plastics Thermocomp YF004 resin is a compound based on Polyestser Elastomer resin containing Glass Fiber.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 51 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 47 | MPa | ASTM D 638 |
| Tensile Strain, break | 11 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 11.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2640 | MPa | ASTM D 638 |
| Flexural Stress | 0 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 55 | MPa | ASTM D 790 |
| Flexural Modulus | 64121250 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1920 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 48 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 12.7 | % | ISO 527 |
| Flexural Stress | 25 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 310 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 401 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | nobreak | kJ/m² | ISO 180/1U |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 151 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, xflow | 3.2E-05 | 1/°C | ASTM D 696 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.35 | - | ASTM D 792 |
| Density | 1.36 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.71 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.34 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.71 | % | ASTM D 955 |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.71 | % | ISO 62 |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.1 | % |
| Melt Temperature | 215 - 240 | °C |
| Front - Zone 3 Temperature | 225 - 240 | °C |
| Middle - Zone 2 Temperature | 205 - 215 | °C |
| Rear - Zone 1 Temperature | 180 - 195 | °C |
| Mold Temperature | 25 - 55 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp YF004.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|