S-Plastics Thermocomp AX06472 resin is a compound based on ABS containing a clay blend.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5930 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 96 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5380 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 240 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 42 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 96 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.3 | - | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.2 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.5 | % | ASTM D 955 |
| ELECTRICAL | Value | Unit | Standard |
| Relative Permittivity, 1 GHz | 3 | - | ASTM D 150 |
| Dissipation Factor, 1 GHz | 0.003 | - | ASTM D 150 |
| Source GMD, last updated:2009/11/24 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 - 0.1 | % |
| Melt Temperature | 260 | °C |
| Front - Zone 3 Temperature | 265 - 275 | °C |
| Middle - Zone 2 Temperature | 230 - 245 | °C |
| Rear - Zone 1 Temperature | 205 - 215 | °C |
| Mold Temperature | 70 - 80 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/11/24 | ||