S-Plastics Thermocomp AS8 resin is compound is a 40% glass bead filled PA 6,6. Automotive - under the hood.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 79 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 79 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.4 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 5320 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 131 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5060 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 352 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 32 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 5 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 236 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 139 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.43 | - | ASTM D 792 |
| Source GMD, last updated:01/04/2002 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 95 - 105 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.07 | % |
| Minimum Moisture Content | 0.02 | % |
| Melt Temperature | 270 - 295 | °C |
| Nozzle Temperature | 270 - 295 | °C |
| Front - Zone 3 Temperature | 265 - 295 | °C |
| Middle - Zone 2 Temperature | 260 - 295 | °C |
| Rear - Zone 1 Temperature | 255 - 295 | °C |
| Mold Temperature | 65 - 95 | °C |
| Back Pressure | 0.3 - 1.4 | MPa |
| Screw Speed | 20 - 100 | rpm |
| Shot to Cylinder Size | 30 - 50 | % |
| Vent Depth | 0.013 - 0.038 | mm |
| Source GMD, last updated:01/04/2002 | ||