S-Plastics Thermocomp AF006XXZ resin is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 96 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.8 | % | ASTM D 638 |
| Flexural Stress | 153 | MPa | ASTM D 790 |
| Flexural Modulus | 9170 | MPa | ASTM D 790 |
| Tensile Stress, break | 83 | MPa | ISO 527 |
| Tensile Strain, break | 1.7 | % | ISO 527 |
| Flexural Stress | 119 | MPa | ISO 178 |
| Flexural Modulus | 8000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 283 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 102 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 102 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.28 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ASTM D 955 |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 - 0.1 | % |
| Melt Temperature | 260 | °C |
| Front - Zone 3 Temperature | 265 - 275 | °C |
| Middle - Zone 2 Temperature | 230 - 245 | °C |
| Rear - Zone 1 Temperature | 205 - 215 | °C |
| Mold Temperature | 70 - 80 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||
Other related products we recommend:
For more information please download the datasheet | |
 | S-Plastics Thermocomp AF006XXZ.pdf |