S-Plastics Thermocomp WFB33E resin isa compound based on Polybutylene Terephalate resin containing Glass Fiber and Glass Bead. Addedfeatures include Easy Molding.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 86 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 132 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4600 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 188 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Source GMD, last updated:11/13/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 240 - 265 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 245 - 255 | °C |
| Rear - Zone 1 Temperature | 220 - 230 | °C |
| Mold Temperature | 80 - 100 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:11/13/2007 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp WFB33E.pdf |
|