S-Plastics Thermocomp PFW53U resin is a compound based on Nylon 6 resin containing Proprietary Filler(s). Added features of this material
include: High Specific Gravity.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 62 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 7490 | MPa | ASTM D 638 |
| Flexural Modulus | 6040 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 283 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 163 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.57 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.6 | % | ASTM D 955 |
| Source GMD, last updated:09/24/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 270 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 250 - 260 | °C |
| Rear - Zone 1 Temperature | 240 - 250 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/24/2008 | ||