S-Plastics Thermocomp WF002resin is a compound based on PBT containing glass fiber.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 77 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 77 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.1 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 5030 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 118 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 121 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4310 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 76 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 76 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.8 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.8 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5020 | MPa | ISO 527 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4360 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 229 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 32 | J/m | ASTM D 256 |
| Multiaxial Impact | 0 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 4 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 213 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 179 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 5.E-06 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 1.E-05 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 212 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 177 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.28 | - | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.08 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 1 - 3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ASTM D 955 |
| Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Source GMD, last updated:05/05/2008 | |||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp WF002.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|