S-Plastics Thermocomp RF005SXS resin is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include:
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 132 | MPa | ASTM D 638 |
| Tensile Strain, break | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 9100 | MPa | ASTM D 638 |
| Flexural Stress | 197 | MPa | ASTM D 790 |
| Flexural Modulus | 7230 | MPa | ASTM D 790 |
| Tensile Stress, break | 139 | MPa | ISO 527 |
| Tensile Strain, break | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8600 | MPa | ISO 527 |
| Flexural Stress | 205 | MPa | ISO 178 |
| Flexural Modulus | 8300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 485 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 69 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 6 | J | ASTM D 3763 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 33 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 258 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 245 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 224 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.346 | g/cm³ | ASTM D 792 |
| Mold Shrinkage, flow, 24 hrs | 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.4 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.34 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.4 | % | ISO 294 |
| Density | 1.34 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:10/02/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/02/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp RF005SXS.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|