S-Plastics Thermocomp UX08030 resin is a compound based on Polyphthalamide resin containing Glass Fiber. Added features include; Hydrolysis Resistant, FDA- and KTW (85C) - compliant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 232 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 14400 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 11100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 70 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 258 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Source GMD, last updated:2010/01/05 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.15 | % |
| Melt Temperature | 315 - 330 | °C |
| Front - Zone 3 Temperature | 325 - 340 | °C |
| Middle - Zone 2 Temperature | 315 - 325 | °C |
| Rear - Zone 1 Temperature | 310 - 320 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2010/01/05 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |