S-Plastics Thermocomp UX06032 resin is a compound based on Polyphthalamide resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Non-Brominated & Non-Chlorinated Flame Retardant, Heat Stabilized.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 160 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11100 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 220 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 265 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.1 - 0.3 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.1 - 0.3 | % | S-Plastics Method |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.5 | % | ISO 62-1 |
| ELECTRICAL | Value | Unit | Standard |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, passes at | 1.5 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 0.8 mm | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.6 mm | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Source GMD, last updated:2006/10/10 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 140 | °C |
| Drying Time | 4 - 6 | hrs |
| Melt Temperature | 305 - 315 | °C |
| Front - Zone 3 Temperature | 295 - 315 | °C |
| Middle - Zone 2 Temperature | 290 - 310 | °C |
| Rear - Zone 1 Temperature | 280 - 300 | °C |
| Mold Temperature | 130 - 150 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 40 - 80 | rpm |
| Source GMD, last updated:2006/10/10 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp UX06032.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|