S-Plastics Thermocomp QF00A resin is PA6.10, Glass Fiber,Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 181 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 181 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 18680 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 280 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 285 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 11440 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 181 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 181 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 15510 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 12870 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1305 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 160 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 75 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 221 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 213 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.5E+00 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.83E+00 | 1/°C | ASTM E 831 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 220 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 205 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.6 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.21 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.18 - 0.2 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 1.5 | % | ASTM D 955 |
| Density | 1.6 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.28 | % | ISO 62 |
| Source GMD, last updated:02/04/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.12 - 0.2 | % |
| Melt Temperature | 270 - 275 | °C |
| Front - Zone 3 Temperature | 270 - 280 | °C |
| Middle - Zone 2 Temperature | 260 - 270 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:02/04/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp QF00A.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|