S-Plastics Thermocomp RFZ349 resin is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this materialinclude: Flame Retardant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 124 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11030 | MPa | ASTM D 638 |
| Flexural Stress | 179 | MPa | ASTM D 790 |
| Flexural Modulus | 7170 | MPa | ASTM D 790 |
| Tensile Stress, break | 85 | MPa | ISO 527 |
| Tensile Strain, break | 3.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11400 | MPa | ISO 527 |
| Flexural Stress | 197 | MPa | ISO 178 |
| Flexural Modulus | 9000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 587 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 64 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 7 | J | ASTM D 3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 39 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 237 | °C | ASTM D 648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 235 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Moisture Absorption, 50% RH, 24 hrs | 0.2 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.2 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.39 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.19 | % | ISO 294 |
| Density | 1.66 | g/cm³ | ISO 1183 |
| Source GMD, last updated:02/27/2007 | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded | |||
| samples. All samples tested under ISO test standards are prepared according to ISO 294. | |||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. |