S-Plastics Thermocomp OC004 resin is a compound based on PPS-Linear resin containing Carbon Fiber. Added features include : Electrically
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 144 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 16600 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 194 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 193 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 1.5 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 15100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 1.3E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 5.5E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 275 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 235 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.15 | % | S-Plastics Method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.04 | % | ISO 62-1 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+01 - 1.E+03 | Ohm | ASTM D 257 |
| Source GMD, last updated:03/05/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 315 - 320 | °C |
| Front - Zone 3 Temperature | 330 - 345 | °C |
| Middle - Zone 2 Temperature | 320 - 330 | °C |
| Rear - Zone 1 Temperature | 305 - 315 | °C |
| Mold Temperature | 140 - 165 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:03/05/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Thermocomp OC004.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|