S-Plastics Thermocomp RFB24 resin is a compound based on PA 66 resin containing Glass Bead, Glass Fiber.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 147 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7800 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 215 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 213 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.01E-04 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 257 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 238 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow (5) | 0.4 | % | S-Plastics Method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 1.2 | % | ISO 62-1 |
| Source GMD, last updated:2009/12/17 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 295 - 305 | °C |
| Middle - Zone 2 Temperature | 280 - 295 | °C |
| Rear - Zone 1 Temperature | 265 - 275 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/12/17 | ||