S-Plastics Thermocomp PH0700B resin is a Nylon 6 base resin containing Tungsten. Characteristics are High Specific Gravity.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 42 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 41 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 10.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 6860 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 62 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3860 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 888 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 106 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 183 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 70 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 7.76E+01 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 7.77E+01 | 1/°C | ASTM D 696 |
| PHYSICAL | Value | Unit | Standard |
| Density | 6.78 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.09 | % | ASTM D 570 |
| Source GMD, last updated:2009/06/09 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 265 - 270 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 250 - 260 | °C |
| Rear - Zone 1 Temperature | 240 - 250 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/06/09 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Thermocomp PH0700B.pdf |
|