S-Plastics Thermocomp MFM43S resin is a compound based on Polypropylene resin containing Glass Fiber, Mineral. Added features include :
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 56 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 86 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 45 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 3.7 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 5100 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 4.4E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.27E-04 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 124 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.2 | % | S-Plastics Method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.01 | % | ISO 62-1 |
| Source GMD, last updated:03/06/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 225 - 250 | °C |
| Front - Zone 3 Temperature | 240 - 250 | °C |
| Middle - Zone 2 Temperature | 215 - 225 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 30 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:03/06/2008 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Thermocomp MFM43S.pdf |
|