S-Plastics Thermocomp MFB44S resin is a compound based on Polypropylene resin containing Glass Fiber, Glass Beads. Added features
include; Heat Stabilized, Cu-Stabilized.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | >1.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 5600 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 65 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4200 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 125 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.1 - 0.3 | % | S-Plastics Method |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Source GMD, last updated:2009/04/07 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 225 - 250 | °C |
| Front - Zone 3 Temperature | 240 - 250 | °C |
| Middle - Zone 2 Temperature | 215 - 225 | °C |
| Rear - Zone 1 Temperature | 195 - 205 | °C |
| Mold Temperature | 30 - 50 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/04/07 | ||