S-Plastics Lexan EXRL0720 resin is Glassfiber reinforced, Flame retardant Polycarbonate (V0/1mm) using Non-Brominated & Non-Chlorinated Flame Retardants. Meets UL
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 65 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 61 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3750 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 104 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*3 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Ball Pressure Test, 125°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/120 | 140 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 130 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 16 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 2 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1 | mm | UL 94 by GE |
| Source GMD, last updated:2009/11/17 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 290 - 320 | °C |
| Nozzle Temperature | 280 - 310 | °C |
| Front - Zone 3 Temperature | 290 - 320 | °C |
| Middle - Zone 2 Temperature | 280 - 310 | °C |
| Rear - Zone 1 Temperature | 270 - 300 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 80 - 120 | °C |
| Source GMD, last updated:2009/11/17 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan EXRL0720.pdf |
|