S-Plastics LexanEXRL0609is A UV Stabilized Standard Flow Polycarbonate Copolymer Resin With Improved Scratch Resistance
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 80 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 63 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 7 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 66 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2600 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 109 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | 82 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 90 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 136 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 137 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 115 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 13 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:01/06/2009 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 295 - 315 | °C |
| Nozzle Temperature | 290 - 310 | °C |
| Front - Zone 3 Temperature | 295 - 315 | °C |
| Middle - Zone 2 Temperature | 280 - 305 | °C |
| Rear - Zone 1 Temperature | 260 - 280 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 70 - 95 | °C |
| Source GMD, last updated:01/06/2009 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan EXRL0609.pdf |
|