S-Plastics Lexan EXRL0606 resin is High flow 9% glass filled ECO-FR PC copolymer
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 4.5 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 10 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3600 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 95 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3400 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*3 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 8 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 145 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 130 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.26 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 13 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:04/21/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 310 - 330 | °C |
| Nozzle Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 310 - 330 | °C |
| Middle - Zone 2 Temperature | 300 - 320 | °C |
| Rear - Zone 1 Temperature | 285 - 310 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 80 - 115 | °C |
| Source GMD, last updated:04/21/2008 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan EXRL0606.pdf |
|