S-Plastics Lexan EXRL0149 resin is PC/SLX Transparent Color Layer for Speciality Film & Sheet business.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 72 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6.5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 125 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2320 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 99 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2420 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 69 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6.2 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 118 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 92 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2310 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 975 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 390 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 86 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 71 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 13 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 89 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 144 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 127 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temp, Rate B/50 | 144 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 146 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 123 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.22 | - | ASTM D 792 |
| Melt Flow Rate, 300°C/1.2 kgf | 5.1 | g/10 min | ASTM D 1238 |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 4 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:02/21/2006 | |||
|
For more information please download the datesheet |
|
 |
S-Plastics Lexan EXRL0149.pdf |
|