S-Plastics Thermotuf CF007IXP resin is a compound based on Polystyrene containing glass fiber. Characteristics of this grade are: High Impact.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 50 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 0.7 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 10230 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 71 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8820 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 44 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8910 | MPa | ISO 527 |
| Flexural Stress | 68 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8760 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 130 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 23 | J/m | ASTM D 256 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 8 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 2 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 97 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 92 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 5.26E+01 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 5.33E+01 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 97 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 92 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Density | 1.3 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.05 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.1 - 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.3 - 0.6 | % | ASTM D 955 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Source GMD, last updated:2009/07/28 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 250 | °C |
| Front - Zone 3 Temperature | 265 - 275 | °C |
| Middle - Zone 2 Temperature | 245 - 255 | °C |
| Rear - Zone 1 Temperature | 220 - 230 | °C |
| Mold Temperature | 40 - 65 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:2009/07/28 | ||
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
Other related products we recommend:
For more information please download the datasheet | |
| S-Plastics Thermotuf CF007IXP.pdf |
Get The Latest Quotation |