S-Plastics Lexan RL6571resin is SINGLE LOT DATA (L37313): 20% glass-reinforced SP grade. Color M73445.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 89 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.4 | % | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 144 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5010 | MPa | ASTM D 790 |
| Hardness, Rockwell M | 66 | - | ASTM D 785 |
| Hardness, Rockwell R | 118 | - | ASTM D 785 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 694 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 7 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 123 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.35 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.24 - 0.45 | % | S-Plastics Method |
| Melt Flow Rate, 300°C/1.2 kgf | 6.3 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:12/29/1999 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Melt Temperature | 270 - 310 | °C |
| Nozzle Temperature | 270 - 300 | °C |
| Front - Zone 3 Temperature | 270 - 300 | °C |
| Middle - Zone 2 Temperature | 270 - 290 | °C |
| Rear - Zone 1 Temperature | 260 - 275 | °C |
| Mold Temperature | 50 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 35 - 75 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Source GMD, last updated:12/29/1999 | ||
For more information please download the datesheet | |
 | S-Plastics Lexan RL6571.pdf |