Sabic Lexan LSHF Clear PolyCarbonate, High Flow, UV Stabilization, Heat Stabilization

100KG
MOQ
*USD
Price
Sabic Lexan LSHF Clear PolyCarbonate, High Flow, UV Stabilization, Heat Stabilization
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 25
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: LSHF
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan LSHF resin is Clear PolyCarbonate, High Flow, UV Stabilization, Heat Stabilization


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 65 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 6 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 110 % ASTM D 638
Tensile Modulus, 5 mm/min 2380 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 93 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2300 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 50 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 70 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 640 J/m ASTM D 256
Izod Impact, notched, -30°C N/A J/m ASTM D 256
Tensile Impact, Type "S" 378 kJ/m² ASTM D 1822
Instrumented Impact Energy @ peak, 23°C 54 J ASTM D 3763
Instrumented Impact Total Energy, 23°C 60 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 60 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 11 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 60 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 12 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 138 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 127 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 126 °C ASTM D 648
CTE, -30°C to 30°C, flow 7.E-05 1/°C ASTM D 696
CTE, -30°C to 30°C, xflow 7.E-05 1/°C ASTM D 696
CTE, 23°C to 80°C, flow 7.E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 139 °C ISO 306
Vicat Softening Temp, Rate B/120 140 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 122 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2) 0.5 - 0.7 % SABIC Method
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Mold Shrinkage, xflow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 25 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 24 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Source GMD, last updated:01/16/2004    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 270 - 295 °C
Nozzle Temperature 265 - 290 °C
Front - Zone 3 Temperature 270 - 295 °C
Middle - Zone 2 Temperature 260 - 280 °C
Rear - Zone 1 Temperature 250 - 270 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:01/16/2004  

 

For more information please download the datasheet

Sabic Lexan LSHF Clear PolyCarbonate, High Flow, UV Stabilization, Heat Stabilization 0  Sabic Lexan LSHF.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan LSHF Clear PolyCarbonate, High Flow, UV Stabilization, Heat Stabilization 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)