Sabic Lexan EXL1413B polycarbonate (PC) siloxane copolymer resin is an opaque injection molding (IM) grade modified

100KG
MOQ
*USD
Price
Sabic Lexan EXL1413B polycarbonate (PC) siloxane copolymer resin is an opaque injection molding (IM) grade modified
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 10
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: EXL1413B
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  EXL1413B resin is polycarbonate (PC) siloxane copolymer resin is an opaque injection molding (IM) grade modified with anti-microbial additives. This resin offers extreme low temperature (-30°C) ductility in combination with medium flow characteristics and excellent
processability with opportunities for shorter IM cycle times compared to standard PC. Lexan EXL1413B resin is available in a standard black color and a standard grey color. Limited other colors available on request.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 55 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 50 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 6 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 98 % ASTM D 638
Tensile Modulus, 50 mm/min 2020 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 92 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2230 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 57 MPa ISO 527
Tensile Stress, break, 50 mm/min 60 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 120 % ISO 527
Tensile Modulus, 1 mm/min 2150 MPa ISO 527
Flexural Stress, yield, 2 mm/min 85 MPa ISO 178
Flexural Modulus, 2 mm/min 2250 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 850 J/m ASTM D 256
Izod Impact, notched, -30°C 760 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 65 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 65 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 25 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 30 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 145 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 124 °C ASTM D 648
CTE, -40°C to 40°C, flow 7.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 7.5E-05 1/°C ASTM E 831
CTE, 23°C to 80°C, flow 7.2E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.2E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 145 °C ISO 306
Vicat Softening Temp, Rate B/120 146 °C ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 128 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Specific Gravity 1.18 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.4 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 10 g/10 min ASTM D 1238
Density 1.19 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 9 cm³/10 min ISO 1133
FLAME CHARACTERISTICS Value Unit Standard
Glow Wire Flammability Index 960°C, passes at 1 mm IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm 900 °C IEC 60695-2-13
Source GMD, last updated:09/29/2005    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 215 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:09/29/2005  

 

 


 

For more information please download the datasheet

Sabic Lexan EXL1413B polycarbonate (PC) siloxane copolymer resin is an opaque injection molding (IM) grade modified 0  Sabic Lexan EXL1413B.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan EXL1413B polycarbonate (PC) siloxane copolymer resin is an opaque injection molding (IM) grade modified 1Click to consult and get the latest quotation within 24 hours!

 