S-Plastics Lexan LR100G1 resin is a 10% glass fibre reinforced material used for non-cosmetic injection moulding applications. The product is designed to utelize recycle materials from our plants, customers and post-consumer materials and is
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3000 | MPa | ISO 527 |
| Flexural Modulus, 2 mm/min | 3000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 143 | °C | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.2 - 0.6 | % | S-Plastics Method |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.31 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.13 | % | ISO 62 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 7 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:1996/02/07 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 290 - 320 | °C |
| Nozzle Temperature | 280 - 310 | °C |
| Front - Zone 3 Temperature | 290 - 320 | °C |
| Middle - Zone 2 Temperature | 280 - 310 | °C |
| Rear - Zone 1 Temperature | 270 - 300 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 80 - 120 | °C |
| Source GMD, last updated:1996/02/07 | ||
|