Sabic Lexan EX1472T Is A UV Stabilized, Medium Viscosity Branched Polycarbonate Grade, Especially Developed

100KG
MOQ
*USD
Price
Sabic Lexan EX1472T Is A UV Stabilized, Medium Viscosity Branched Polycarbonate Grade, Especially Developed
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Volume Rate, MVR At 300°C/1.2 Kg: 7
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: EX1472T
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  EX1472T resin is a UV stabilized, medium viscosity branched polycarbonate grade, especially developed for the extrusion of complex
sheet structures.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy SABIC Method
Tensile Stress, yield, 50 mm/min 60 MPa ISO 527
Tensile Stress, break, 50 mm/min 65 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 110 % ISO 527
Tensile Modulus, 1 mm/min 2300 MPa ISO 527
Flexural Stress, yield, 2 mm/min 100 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 65 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 12 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 13 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Thermal Conductivity 0.2 W/m-°C ISO 8302
CTE, -40°C to 40°C, flow 7.E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate A/50 148 °C ISO 306
Vicat Softening Temp, Rate B/50 146 °C ISO 306
Vicat Softening Temp, Rate B/120 143 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 136 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 124 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Mold Shrinkage on Tensile Bar, flow (2) 0.5 - 0.7 % SABIC Method
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.35 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 7 cm³/10 min ISO 1133
Melt Volume Rate, MVR at 300°C/2.16 kg 12 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Haze <0.8 % ASTM D 1003
Source GMD, last updated:05/10/2006    

Processing

Processing    
Parameter    
Profile Extrusion Value Unit
Drying Temperature 120 °C
Drying Time 2 - 4 hrs
Melt Temperature 280 - 300 °C
Barrel - Zone 1 Temperature 240 - 280 °C
Barrel - Zone 2 Temperature 260 - 290 °C
Barrel - Zone 3 Temperature 260 - 290 °C
Barrel - Zone 4 Temperature 260 - 290 °C
Hopper Temperature 100 - 120 °C
Adapter Temperature 270 - 300 °C
Die Temperature 260 - 290 °C
Calibrator Temperature 80 - 100 °C
Source GMD, last updated:05/10/2006  

 


 

For more information please download the datasheet

Sabic Lexan EX1472T Is A UV Stabilized, Medium Viscosity Branched Polycarbonate Grade, Especially Developed 0  Sabic Lexan EX1472T.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan EX1472T Is A UV Stabilized, Medium Viscosity Branched Polycarbonate Grade, Especially Developed 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)