Sabic Lexan DMX9254 resin is an injection moldable PC copolymer/ABS blend. This resin combines excellent scratch resista

100KG
MOQ
*USD
Price
Sabic Lexan DMX9254 resin is an injection moldable PC copolymer/ABS blend. This resin combines excellent scratch resista
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 29
UL Recognized, 94V-1 Flame Class Rating (3): 1
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: DMX9254
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  DMX9254 resin is an injection moldable PC copolymer/ABS blend. This resin combines excellent scratch resistance with high flow and ductility. It contains non-brominated and non-chlorinated flame retardant systems to meet UL-94 V0 at 1.5mm and V1 at 1.0mm.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 72 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 55 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 4.8 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 65 % ASTM D 638
Tensile Modulus, 50 mm/min 3150 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 109 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2750 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 3050 MPa ISO 527
Tensile Stress, break, 50 mm/min 53 MPa ISO 527
Tensile Strain, yield, 50 mm/min 4.7 % ISO 527
Tensile Strain, break, 50 mm/min 75 % ISO 527
Tensile Modulus, 1 mm/min 2850 MPa ISO 527
Flexural Stress, yield, 2 mm/min 105 MPa ISO 178
Flexural Modulus, 2 mm/min 2700 MPa ISO 178
Pencil Hardness test, 1kgf F - ASTM D 3363
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 42 J/m ASTM D 256
Izod Impact, notched, -30°C 25 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 56 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C 53 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 6 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 5 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 7 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 5 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm 59 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 105 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 98 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 87 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 6.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 6.E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 6.E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 104 °C ISO 306
Vicat Softening Temp, Rate B/120 107 °C ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 98 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 88 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.19 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 260°C/2.16 kgf 15 g/10 min ASTM D 1238
Melt Flow Rate, 300°C/1.2 kgf 29 g/10 min ASTM D 1238
Density 1.19 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.1 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.1 % ISO 62
Melt Volume Rate, MVR at 260°C/2.16 kg 12 cm³/10 min ISO 1133
Melt Volume Rate, MVR at 300°C/1.2 kg 25 cm³/10 min ISO 1133
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-1 Flame Class Rating (3) 1 mm UL 94
UL Recognized, 94V-0 Flame Class Rating (3) 1.5 mm UL 94
Source GMD, last updated:11/01/2006    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 80 - 90 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.04 %
Melt Temperature 245 - 275 °C
Nozzle Temperature 245 - 275 °C
Front - Zone 3 Temperature 245 - 275 °C
Middle - Zone 2 Temperature 220 - 265 °C
Rear - Zone 1 Temperature 220 - 255 °C
Mold Temperature 60 - 80 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 30 - 80 %
Vent Depth 0.038 - 0.076 mm
Source GMD, last updated:11/01/2006  

 

 


 

For more information please download the datasheet

Sabic Lexan DMX9254 resin is an injection moldable PC copolymer/ABS blend. This resin combines excellent scratch resista 0  Sabic Lexan DMX9254.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan DMX9254 resin is an injection moldable PC copolymer/ABS blend. This resin combines excellent scratch resista 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)