Sabic Lexan DMX1415 Is A Copolycarbonate Resin With Improved Scratch Resistance. Lexan* DMX1415 Is Available In Transpar

100KG
MOQ
*USD
Price
Sabic Lexan DMX1415 Is A Copolycarbonate Resin With Improved Scratch Resistance. Lexan* DMX1415 Is Available In Transpar
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 14.5
UL Recognized, 94V-2 Flame Class Rating (3): 0.4
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: DMX1415
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  DMX1415 resin is a copolycarbonate resin with improved scratch resistance. Lexan* DMX1415 is available in transparent and
translucent colors.


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 80 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 65 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 70 % ASTM D 638
Tensile Modulus, 50 mm/min 2900 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 120 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2600 MPa ASTM D 790
Hardness, Rockwell L 108 - ASTM D 785
Hardness, Rockwell M 93 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy SABIC Method
Tensile Stress, yield, 50 mm/min 80 MPa ISO 527
Tensile Stress, break, 50 mm/min 60 MPa ISO 527
Tensile Strain, yield, 50 mm/min 7 % ISO 527
Tensile Strain, break, 50 mm/min 40 % ISO 527
Tensile Modulus, 1 mm/min 2450 MPa ISO 527
Flexural Stress, yield, 2 mm/min 108 MPa ISO 178
Flexural Modulus, 2 mm/min 2450 MPa ISO 178
Hardness, H358/30 128 MPa ISO 2039-1
Pencil Hardness test, 1kgf H - ASTM D 3363
Erichson scratch depth, 6N 14 micrometer SABIC Method
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C NB J/m ASTM D 4812
Izod Impact, notched, 23°C 30 J/m ASTM D 256
Izod Impact, notched, -30°C 30 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 30 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C 45 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 5 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 4 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 3 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 3 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm 47 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 139 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 133 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 119 °C ASTM D 648
CTE, -40°C to 95°C, flow 7.E-05 1/°C ASTM E 831
CTE, -40°C to 95°C, xflow 7.E-05 1/°C ASTM E 831
Specific Heat 1.4 J/g-°C ASTM C 351
Thermal Conductivity 0.2 W/m-°C ASTM C 177
Thermal Conductivity 0.2 W/m-°C ISO 8302
CTE, 23°C to 80°C, flow 7.E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Ball Pressure Test, approximate maximum 140 °C IEC 60695-10-2
Vicat Softening Temp, Rate B/50 138 °C ISO 306
Vicat Softening Temp, Rate B/120 140 °C ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 131 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 118 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Specific Volume 0.85 cm³/g ASTM D 792
Density 1.17 g/cm³ ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 14.5 g/10 min ASTM D 1238
Density 1.17 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.27 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.13 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 13 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Haze <0.8 % ASTM D 1003
Refractive Index 1.584 - ASTM D 542
Refractive Index 1.584 - ISO 489
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+17 Ohm-cm ASTM D 257
Relative Permittivity, 50/60 Hz 2.9 - ASTM D 150
Relative Permittivity, 1 MHz 2.8 - ASTM D 150
Comparative Tracking Index (UL) {PLC} 2 PLC Code UL 746A
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94HB Flame Class Rating (3) 0.4 mm UL 94
Source GMD, last updated:05/21/2008    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 260 - 280 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 70 - 95 °C
Source GMD, last updated:05/21/2008  

 


 

For more information please download the datasheet

Sabic Lexan DMX1415 Is A Copolycarbonate Resin With Improved Scratch Resistance. Lexan* DMX1415 Is Available In Transpar 0  Sabic Lexan DMX1415.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan DMX1415 Is A Copolycarbonate Resin With Improved Scratch Resistance. Lexan* DMX1415 Is Available In Transpar 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)