Sabic Lexan DMX1214 Resin Is An Improved Flow, Transparent Copolycarbonate Resin With Improved Scratch Resistance.

100KG
MOQ
*USD
Price
Sabic Lexan DMX1214 Resin Is An Improved Flow, Transparent Copolycarbonate Resin With Improved Scratch Resistance.
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 17.1
UL Recognized, 94V-2 Flame Class Rating (3): 0.75
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: DMX1214
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  DMX1214 resin is an improved flow, transparent copolycarbonate resin with improved scratch resistance.

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 77 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 64 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 92 % ASTM D 638
Tensile Modulus, 50 mm/min 2830 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 116 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2630 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 77 MPa ISO 527
Tensile Stress, break, 50 mm/min 62 MPa ISO 527
Tensile Strain, yield, 50 mm/min 8 % ISO 527
Tensile Strain, break, 50 mm/min 60 % ISO 527
Tensile Modulus, 1 mm/min 2400 MPa ISO 527
Flexural Stress, yield, 2 mm/min 101 MPa ISO 178
Flexural Modulus, 2 mm/min 2310 MPa ISO 178
Pencil Hardness test, 1kgf F - ASTM D 3363
Erichson scratch depth, 6N 14 micrometer SABIC Method
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C NB J/m ASTM D 4812
Izod Impact, notched, 23°C 37 J/m ASTM D 256
Izod Impact, notched, -30°C 32 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 68 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C 93 kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 6 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 4 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 3 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 3 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm 133 kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 138 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 133 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 121 °C ASTM D 648
CTE, -40°C to 95°C, flow 6.E-05 1/°C ASTM E 831
CTE, -40°C to 95°C, xflow 6.E-05 1/°C ASTM E 831
CTE, 23°C to 80°C, flow 6.E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 6.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C Pass - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 141 °C ISO 306
Vicat Softening Temp, Rate B/120 142 °C ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 134 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 121 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.18 - ASTM D 792
Specific Volume 0.85 cm³/g ASTM D 792
Density 1.17 g/cm³ ASTM D 792
Water Absorption, 24 hours 0.1 % ASTM D 570
Water Absorption, equilibrium, 23C 0.3 % ASTM D 570
Water Absorption, 50% RH, equilib 0.14 % ASTM D 570
Moisture Absorption, 50% RH, 24 hrs 0.05 % ASTM D 570
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 17.1 g/10 min ASTM D 1238
Density 1.17 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.3 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.14 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 16 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Haze <0.8 % ASTM D 1003
Refractive Index 1.584 - ASTM D 542
Refractive Index 1.584 - ISO 489
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94HB Flame Class Rating (3) 0.75 mm UL 94
Source GMD, last updated:03/27/2007    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 260 - 280 °C
Hopper Temperature 60 - 80 °C
Mold Temperature 70 - 95 °C
Source GMD, last updated:03/27/2007  

 


 

For more information please download the datasheet

Sabic Lexan DMX1214 Resin Is An Improved Flow, Transparent Copolycarbonate Resin With Improved Scratch Resistance. 0  Sabic Lexan DMX1214.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan DMX1214 Resin Is An Improved Flow, Transparent Copolycarbonate Resin With Improved Scratch Resistance. 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)