S-Plastics Lexan ML3046 resin isImpact modified, for applications requiring improved ductility at lower temp., Available in wide range of opaque colours.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 55 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 8 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1900 | MPa | ASTM D 638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 90 | MPa | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 2000 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 600 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 550 | J/m | ASTM D 256 |
| Izod Impact, notched, -40°C | 500 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 60 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 55 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 55 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy Impact, notched, 23°C | 40 | kJ/m² | ISO 179/2C |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 150 | °C | ASTM D 1525 |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/120 | 135 | °C | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.6 - 0.8 | % | S-Plastics Method |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 |
| Source GMD, last updated:02/24/2003 | |||
| Injection Molding | Value | Unit | |
| Drying Temperature | 120 | °C | |
| Drying Time | 2 - 4 | hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 280 - 310 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Front - Zone 3 Temperature | 280 - 310 | °C | |
| Middle - Zone 2 Temperature | 270 - 290 | °C | |
| Rear - Zone 1 Temperature | 260 - 280 | °C | |
| Hopper Temperature | 60 - 80 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Source GMD, last updated:02/24/2003 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
|
For more information please download the datasheet |
|
 |
S-Plastics Lexan ML3046.pdf |
|