Sabic Lexan ML1913 9% Glass-Filled PC For Automotive Applications

100KG
MOQ
*USD
Price
Sabic Lexan ML1913 9% Glass-Filled PC For Automotive Applications
Features Gallery Product Description Request A Quote
Features
Specifications
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: ML1913
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  ML1913 resin is9% glass-filled PC. For automotive applications.

Property

 

MECHANICAL Value Unit Standard
Tensile Stress, brk, Type I, 5 mm/min 64 MPa ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 15 % ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 102 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 3370 MPa ASTM D 790
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 85 J/m ASTM D 256
Falling Dart Impact, 23°C 101 J SABIC Method
THERMAL Value Unit Standard
HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648
PHYSICAL Value Unit Standard
Specific Gravity 1.28 - ASTM D 792
Water Absorption, 24 hours 0.09 % ASTM D 570
Source GMD, last updated:12/29/1999    

Processing

Injection Molding Value Unit  
Drying Temperature 120 °C  
Drying Time 3 - 4 hrs  
Drying Time (Cumulative) 48 hrs  
Maximum Moisture Content 0.02 %  
Melt Temperature 295 - 315 °C  
Nozzle Temperature 290 - 310 °C  
Front - Zone 3 Temperature 295 - 315 °C  
Middle - Zone 2 Temperature 280 - 305 °C  
Rear - Zone 1 Temperature 270 - 295 °C  
Mold Temperature 70 - 95 °C  
Back Pressure 0.3 - 0.7 MPa  
Screw Speed 40 - 70 rpm  
Shot to Cylinder Size 40 - 60 %  
Vent Depth 0.025 - 0.076 mm  
Source GMD, last updated:12/29/1999    
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.    
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION    
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.      
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.      
(4) Internal measurements according to UL standards.      

 

For more information please download the datasheet

Sabic Lexan ML1913 9% Glass-Filled PC For Automotive Applications 0  Sabic Lexan ML1913.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan ML1913 9% Glass-Filled PC For Automotive Applications 1Click to consult and get the latest quotation within 24 hours!

 