Sabic Lexan ML1665 Polycarbonate For Aircraft Applications Requiring FAR 25.853a Compliance For Extrusion And Injection

100KG
MOQ
*USD
Price
Sabic Lexan ML1665 Polycarbonate For Aircraft Applications Requiring FAR 25.853a Compliance For Extrusion And Injection
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 7.3
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: ML1665
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  ML1665 resin is Polycarbonate for aircraft applications requiring FAR 25.853a compliance. For extrusion and injection molding applications. Opaque colors only


Property

MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 90 % ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 91 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2240 MPa ASTM D 790
Hardness, Rockwell R 118 - ASTM D 785
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 3204 J/m ASTM D 4812
Izod Impact, notched, 23°C 640 J/m ASTM D 256
THERMAL Value Unit Standard
HDT, 0.45 MPa, 6.4 mm, unannealed 137 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648
PHYSICAL Value Unit Standard
Specific Gravity2````````` 1.21 - ASTM D 792
Water Absorption, 24 hours 0.15 % ASTM D 570
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 7.3 g/10 min ASTM D 1238
Source GMD, last updated:01/04/2000    

Processing

Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 5 hrs
Drying Time (Cumulative) 48 hrs
Melt Temperature 315 - 345 °C
Nozzle Temperature 305 - 330 °C
Front - Zone 3 Temperature 315 - 340 °C
Middle - Zone 2 Temperature 295 - 315 °C
Rear - Zone 1 Temperature 290 - 305 °C
Mold Temperature 80 - 115 °C
Back Pressure 0.3 - 1.4 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.038 - 0.076 mm
Source GMD, last updated:01/04/2000  
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.  
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION    
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
   
(2) Only typical data for selection purposes. Not to be used for part or tool design.    
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.    
(4) Internal measurements according to UL standards.    

 

For more information please download the datasheet

Sabic Lexan ML1665 Polycarbonate For Aircraft Applications Requiring FAR 25.853a Compliance For Extrusion And Injection 0  Sabic Lexan ML1665.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan ML1665 Polycarbonate For Aircraft Applications Requiring FAR 25.853a Compliance For Extrusion And Injection 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)