S-Plastics Lexan FXG154 resin is FXG154 is a Lexan PC grade with the Diamond effect. Color Package may affect properties, Application testing always recommended.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 58 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 57 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 5.9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 39 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2680 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 98 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2390 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 61 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 54 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 6.2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 75 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2430 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 94 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2340 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 752 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 142 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 62 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 51 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 16 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 58 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 153 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 133 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 147 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 149 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 129 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 200°C/3.8 kgf | 2.5 | g/10 min | ASTM D 1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.15 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.09 | % | ISO 62 |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 2 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:03/14/2007 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Minimum Moisture Content | 0.01 | % |
| Melt Temperature (Parison) | 265 - 280 | °C |
| Barrel - Zone 1 Temperature | 260 - 290 | °C |
| Barrel - Zone 2 Temperature | 260 - 290 | °C |
| Barrel - Zone 3 Temperature | 260 - 290 | °C |
| Barrel - Zone 4 Temperature | 260 - 290 | °C |
| Adapter - Zone 5 Temperature | 260 - 290 | °C |
| Mold Temperature | 60 - 100 | °C |
| Source GMD, last updated:03/14/2007 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Lexan EXRL0687.pdf |
|