Sabic Lexan IR2220 10.5 MFR Transparent/Opaque PC. Mold Release And Heat Stabilized.

100KG
MOQ
*USD
Price
Sabic Lexan IR2220 10.5 MFR Transparent/Opaque PC. Mold Release And Heat Stabilized.
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 10.5
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: IR2220
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  IR2220 resin is 10.5 MFR Transparent/Opaque PC. Mold Release and Heat Stabilized.


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 68 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 130 % ASTM D 638
Tensile Modulus, 50 mm/min 2410 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 96 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 65 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 100 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 3204 J/m ASTM D 4812
Izod Impact, notched, 23°C 801 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 63 J ASTM D 3763
Izod Impact, notched 80*10*4 +23°C 59 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT, 1.82 MPa, 3.2mm, unannealed 125 °C ASTM D 648
Specific Heat 1.25 J/g-°C ASTM C 351
Thermal Conductivity 0.27 W/m-°C ASTM C 177
Vicat Softening Temp, Rate B/120 142 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 126 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Water Absorption, equilibrium, 23C 0.35 % ASTM D 570
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 10.5 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Melt Volume Rate, MVR at 300°C/1.2 kg 10 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Haze 1 % ASTM D 1003
Refractive Index 1.586 - ASTM D 542
Source GMD, last updated:12/18/2003    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 - 315 °C
Nozzle Temperature 290 - 310 °C
Front - Zone 3 Temperature 295 - 315 °C
Middle - Zone 2 Temperature 280 - 305 °C
Rear - Zone 1 Temperature 270 - 295 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:12/18/2003  

 


 

For more information please download the datasheet

Sabic Lexan IR2220 10.5 MFR Transparent/Opaque PC. Mold Release And Heat Stabilized. 0  Sabic Lexan IR2220.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan IR2220 10.5 MFR Transparent/Opaque PC. Mold Release And Heat Stabilized. 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)