S-Plastics Lexan FXE1643 resin is an extrusion blow moulding grade in visual effect Energy especially developed for refillable containers for water, juicesand milk. It offers high melt strength, impact resistance and is in compliance with FDA and European regulations concerning food contact applications.
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 60 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 7 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 120 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
| Hardness, H358/30 | 95 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*3 +23°C | 70 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 12 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 73 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 14 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 146 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 143 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 136 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 124 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.5 - 0.7 | % | S-Plastics Method |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Melt Volume Rate, MVR at 280°C/3.8 kg | 2 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 2.7 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 850°C, passes at | 1 | mm | IEC 60695-2-12 |
| Source GMD, last updated:03/20/2003 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature (Parison) | 260 - 280 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Barrel - Zone 1 Temperature | 260 - 290 | °C |
| Barrel - Zone 2 Temperature | 260 - 280 | °C |
| Barrel - Zone 3 Temperature | 260 - 280 | °C |
| Accumulator Temperature | 260 - 280 | °C |
| Mold Temperature | 60 - 80 | °C |
| Die Temperature | 260 - 280 | °C |
| Source GMD, last updated:03/20/2003 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Lexan FXE1643.pdf |
|