Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 5
Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: HPS7R
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Lexan  HPS7R resin is Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 72 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 6.5 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 125 % ASTM D 638
Tensile Modulus, 50 mm/min 2270 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 100 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 61 MPa ISO 527
Tensile Stress, break, 50 mm/min 71 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5.9 % ISO 527
Tensile Strain, break, 50 mm/min 126 % ISO 527
Tensile Modulus, 1 mm/min 2450 MPa ISO 527
Flexural Stress, yield, 2 mm/min 95 MPa ISO 178
Flexural Modulus, 2 mm/min 2200 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 2700 J/m ASTM D 4812
Izod Impact, notched, 23°C 935 J/m ASTM D 256
Izod Impact, notched, -30°C 785 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 82 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 75 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 15 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 75 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 15 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 145 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 141 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 129 °C ASTM D 648
CTE, -40°C to 40°C, flow 6.6E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 7.5E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 6.6E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 7.5E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 145 °C ISO 306
Vicat Softening Temp, Rate B/120 146 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 128 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 300°C/1.2 kgf 5 g/10 min ASTM D 1238
Melt Flow Rate, 300°C/5.0 kgf 24 g/10 min ASTM D 1238
Density 1.19 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.26 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.1 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 5 cm³/10 min ISO 1133
Source GMD, last updated:11/11/2005    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 310 - 330 °C
Nozzle Temperature 305 - 325 °C
Front - Zone 3 Temperature 310 - 330 °C
Middle - Zone 2 Temperature 300 - 320 °C
Rear - Zone 1 Temperature 290 - 310 °C
Mold Temperature 80 - 115 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:11/11/2005  

 


 

For more information please download the datasheet

S-Plastic Lexan HPS7R Low Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare Management 0  S-Plastics Lexan HPS7R.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

S-Plastic Lexan HPS7R Low Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare Management 1Click to consult and get the latest quotation within 24 hours!

 

S-Plastics lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)