S-Plastic Lexan HPS2 Med/High Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare Management

100KG
MOQ
*USD
Price
S-Plastic Lexan HPS2 Med/High Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare Management
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 17.5
Basic Infomation
Place of Origin: ——
Brand Name: S-Plastic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: HPS2
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

S-Plastics Lexan HPS2 resin isMed/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 68 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 125 % ASTM D 638
Tensile Modulus, 50 mm/min 2370 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 96 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2130 MPa ASTM D 790
Hardness, Rockwell M 70 - ASTM D 785
Hardness, Rockwell R 118 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 10 mg/1000cy ASTM D 1044
Tensile Stress, yield, 50 mm/min 63 MPa ISO 527
Tensile Stress, break, 50 mm/min 65 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 100 % ISO 527
Tensile Modulus, 1 mm/min 2350 MPa ISO 527
Flexural Stress, yield, 2 mm/min 90 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 3204 J/m ASTM D 4812
Izod Impact, notched (natural, tints) 694 J/m ASTM D 256
Izod Impact, notched (colors) 106 - 694 J/m ASTM D 256
Tensile Impact, Type "S" 472 kJ/m² ASTM D 1822
Falling Dart Impact (D 3029), 23°C 169 J ASTM D 3029
Instrumented Impact Energy @ peak, 23°C 62 J ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*4 +23°C 12 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 10 kJ/m² ISO 179/1eA
Charpy Impact, notched, 23°C 35 kJ/m² ISO 179/2C
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
HDT, 0.45 MPa, 6.4 mm, unannealed 137 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 129 °C ASTM D 648
CTE, -40°C to 95°C, flow 6.84E-05 1/°C ASTM E 831
Specific Heat 1.25 J/g-°C ASTM C 351
Thermal Conductivity 0.19 W/m-°C ASTM C 177
Thermal Conductivity 0.2 W/m-°C ISO 8302
CTE, 23°C to 80°C, flow 7.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 140 °C ISO 306
Vicat Softening Temp, Rate B/120 141 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 133 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 122 °C ISO 75/Ae
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Specific Volume 0.83 cm³/g ASTM D 792
Density 1.19 g/cm³ ASTM D 792
Water Absorption, 24 hours 0.15 % ASTM D 570
Water Absorption, equilibrium, 23C 0.35 % ASTM D 570
Water Absorption, equilibrium, 100°C 0.58 % ASTM D 570
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 300°C/1.2 kgf 17.5 g/10 min ASTM D 1238
Melt Volume Rate, MVR at 300°C/1.2 kg 16 cm³/10 min ISO 1133
OPTICAL Value Unit Standard
Light Transmission 88 % ASTM D 1003
Haze 1 % ASTM D 1003
Refractive Index 1.586 - ASTM D 542
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+17 Ohm-cm ASTM D 257
Dielectric Strength, in air, 3.2 mm 14.9 kV/mm ASTM D 149
Relative Permittivity, 50/60 Hz 3.17 - ASTM D 150
Relative Permittivity, 1 MHz 2.96 - ASTM D 150
Dissipation Factor, 50/60 Hz 0.0009 - ASTM D 150
Dissipation Factor, 1 MHz 0.01 - ASTM D 150
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 3.2 mm 17 kV/mm IEC 60243-1
Relative Permittivity, 50/60 Hz 2.7 - IEC 60250
Relative Permittivity, 1 MHz 2.7 - IEC 60250
Dissipation Factor, 50/60 Hz 0.001 - IEC 60250
Dissipation Factor, 1 MHz 0.01 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
Oxygen Index (LOI) 25 % ISO 4589
Source GMD, last updated:01/04/2000    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 280 - 305 °C
Nozzle Temperature 275 - 300 °C
Front - Zone 3 Temperature 280 - 305 °C
Middle - Zone 2 Temperature 270 - 295 °C
Rear - Zone 1 Temperature 260 - 280 °C
Mold Temperature 70 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:01/04/2000  

 


 

For more information please download the datasheet

S-Plastic Lexan HPS2 Med/High Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare Management 0  S-Plastics Lexan HPS2.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

S-Plastic Lexan HPS2 Med/High Flow Polycarbonate. For Medical Devices And Pharmaceutical Applications. Healthcare Management 1Click to consult and get the latest quotation within 24 hours!

 

S-Plastics lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)