Sabic Lexan 4301 A High Heat Resistant Poly (Ester) Carbonate Resin For Injection Molding

100KG
MOQ
*USD
Price
Sabic Lexan 4301 A High Heat Resistant Poly (Ester) Carbonate Resin For Injection Molding
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 8
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: 4301
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  4301 resin is a high heat resistant poly (ester) carbonate resin for injection molding
 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 64 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 69 MPa ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 7 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min >50 % ASTM D 638
Tensile Modulus, 5 mm/min 2100 MPa ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 95 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2200 MPa ASTM D 790
Tensile Stress, yield, 50 mm/min 65 MPa ISO 527
Tensile Stress, break, 50 mm/min 60 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 85 % ISO 527
Tensile Modulus, 1 mm/min 2150 MPa ISO 527
Flexural Stress, yield, 2 mm/min 100 MPa ISO 178
Flexural Modulus, 2 mm/min 2300 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 600 J/m ASTM D 256
Izod Impact, notched, -30°C 125 J/m ASTM D 256
Instrumented Impact Total Energy, 23°C 120 J ASTM D 3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 45 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 11 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 50 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 12 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 162 °C ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed 139 °C ASTM D 648
CTE, -40°C to 40°C, flow 8.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 8.E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, flow 8.E-05 1/°C ISO 11359-2
CTE, -40°C to 40°C, xflow 8.E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C pass - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 151 °C ISO 306
Vicat Softening Temp, Rate B/120 153 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 134 °C ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.6 - 0.8 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 8 g/10 min ASTM D 1238
Density 1.2 g/cm³ ISO 1183
Water Absorption, (23°C/sat) 0.16 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.35 % ISO 62
Melt Volume Rate, MVR at 330°C/2.16kg 40 cm³/10 min ISO 1133
Source GMD, last updated:11/08/2004    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 2 - 4 hrs
Melt Temperature 300 - 330 °C
Mold Temperature 100 - 120 °C
Source GMD, last updated:11/08/2004  

 


 

For more information please download the datasheet

Sabic Lexan 4301 A High Heat Resistant Poly (Ester) Carbonate Resin For Injection Molding 0  Sabic Lexan 4301.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan 4301 A High Heat Resistant Poly (Ester) Carbonate Resin For Injection Molding 1Click to consult and get the latest quotation within 24 hours!

 