S-Plastics Lexan 123HSR resin is Easy flow, UV stabilised, super release grade polycarbonate.
TYPICAL PROPERTIES (1) | |||
MECHANICAL | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min | 65 | MPa | ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min | 66 | MPa | ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min | 143 | % | ASTM D 638 |
Tensile Modulus, 50 mm/min | 2340 | MPa | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 97 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2300 | MPa | ASTM D 790 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched, 23°C | 801 | J/m | ASTM D 256 |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp, Rate B/50 | 141 | °C | ASTM D 1525 |
HDT, 1.82 MPa, 3.2mm, unannealed | 123 | °C | ASTM D 648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 133 | °C | ASTM D 648 |
CTE, -40°C to 60°C, flow | 1.26E-04 | 1/°C | ASTM E 831 |
Relative Temp Index, Elec | 130 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 125 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.2 | - | ASTM D 792 |
Water Absorption, 24 hours | 0.15 | % | ASTM D 570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
Melt Flow Rate, 300°C/1.2 kgf | 18 | g/10 min | ASTM D 1238 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | 1.E+15 | Ohm-cm | ASTM D 257 |
Surface Resistivity | 1.E+15 | Ohm | ASTM D 257 |
Relative Permittivity, 50/60 Hz | 0 | - | ASTM D 150 |
Relative Permittivity, 1 MHz | 0.01 | - | ASTM D 150 |
Dissipation Factor, 50/60 Hz | 2.7 | - | ASTM D 150 |
Dissipation Factor, 1 MHz | 2.7 | - | ASTM D 150 |
Comparative Tracking Index | 250 | V | IEC 60112 |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Recognized, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 |
Source GMD, last updated:06/18/1999 |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 3 - 4 | hrs |
Drying Time (Cumulative) | 48 | hrs |
Melt Temperature | 280 - 305 | °C |
Mold Temperature | 70 - 95 | °C |
Source GMD, last updated:06/18/1999 |
For more information please download the datasheet |
|
![]() |
S-Plastics Lexan 123HSR.pdf |