Sabic Lexan 105 General Purpose Low Flow Polycarbonate Powder Grade

100KG
MOQ
*USD
Price
Sabic Lexan 105 General Purpose Low Flow Polycarbonate Powder Grade
Features Gallery Product Description Request A Quote
Features
Specifications
Melt Flow Rate, 300°C/1.2 Kgf: 7
Basic Infomation
Place of Origin: ——
Brand Name: Sabic Lexan
Certification: COA/ICP Test/Rohs/MSDS
Model Number: 105
Payment & Shipping Terms
Packaging Details: 25KG/BAG
Delivery Time: To be negotiated
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: To be negotiated
Product Description

Sabic Lexan  105 resin isGeneral purpose low flow Polycarbonate powder grade

 


Property

TYPICAL PROPERTIES (1)      
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 62 MPa ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 68 MPa ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min >70 % ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 97 MPa ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 2340 MPa ASTM D 790
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C NB J/m ASTM D 4812
Izod Impact, notched, 23°C 907 J/m ASTM D 256
Instrumented Impact Energy @ peak, 23°C 64 J ASTM D 3763
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 154 °C ASTM D 1525
HDT, 0.45 MPa, 6.4 mm, unannealed 137 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 132 °C ASTM D 648
CTE, -40°C to 95°C, flow 6.84E-05 1/°C ASTM E 831
PHYSICAL Value Unit Standard
Specific Gravity 1.2 - ASTM D 792
Density 1.19 g/cm³ ASTM D 792
Water Absorption, equilibrium, 23C 0.35 % ASTM D 570
Water Absorption, equilibrium, 100°C 0.58 % ASTM D 570
Mold Shrinkage, flow, 3.2 mm (5) 0.5 - 0.7 % SABIC Method
Melt Flow Rate, 300°C/1.2 kgf 7 g/10 min ASTM D 1238
OPTICAL Value Unit Standard
Light Transmission, 2.54 mm 88 % ASTM D 1003
Haze, 2.54 mm 1 % ASTM D 1003
Source GMD, last updated:2009/11/09    

Processing

Parameter    
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 310 - 330 °C
Nozzle Temperature 305 - 325 °C
Front - Zone 3 Temperature 310 - 330 °C
Middle - Zone 2 Temperature 300 - 320 °C
Rear - Zone 1 Temperature 290 - 310 °C
Mold Temperature 80 - 115 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:2009/11/09  

 


 

For more information please download the datasheet

Sabic Lexan 105 General Purpose Low Flow Polycarbonate Powder Grade 0  Sabic Lexan 105.pdf

 

Get The Latest Quotation

 

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

 

Sabic Lexan 105 General Purpose Low Flow Polycarbonate Powder Grade 1Click to consult and get the latest quotation within 24 hours!

 

sabic lexan pc products

 

Free Talk 24hours

Recommended Products
Get in touch with us
Tel : 86-13925273675
Characters Remaining(20/3000)