SabikLexanLR505 resin adalah10% Serat kaca diperkuat, PC tahan api dengan sistem FR non-klorinasi dan non-brominasi.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 42 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 20 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3200 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 95 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3100 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 58 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 43 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 33 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3600 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 99 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3400 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 100 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 75 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 44 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 8 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 143 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 133 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 4.1E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.7E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 4.3E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 8.1E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 144 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 146 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 136 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.26 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.3 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.3 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 300°C/1,2 kgf | 7.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.26 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.24 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 300°C/1,2 kg | 6 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 2.3 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:09/30/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 48 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 310 - 330 | °C |
| Suhu Nozzle | 305 - 325 | °C |
| Suhu depan - Zona 3 | 310 - 330 | °C |
| Tengah - Zona 2 Suhu | 300 - 320 | °C |
| Bagian belakang - Zona 1 Suhu | 290 - 310 | °C |
| Suhu Cetakan | 80 - 115 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:09/30/2004 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
SS-Plastics Lexan LR505.pdf |
|