Sabic Lexan121SRMresin adalahAliran mudah, dampak dimodifikasi, super pelepasan kelas polikarbonat.
Properti Tipikal (1) | |||
Mekanis | Nilai | Satuan | Standar |
Tekanan tarik, yld, tipe I, 50 mm/menit | 65 | MPa | ASTM D 638 |
Tekanan tarik, brk, tipe I, 50 mm/menit | 143 | % | ASTM D 638 |
Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 97 | MPa | ASTM D 790 |
Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2300 | MPa | ASTM D 790 |
Dampak | Nilai | Satuan | Standar |
Izod Dampak, bertanduk, 23°C | 801 | J/m | ASTM D 256 |
Termal | Nilai | Satuan | Standar |
HDT, 1,82 MPa, 3,2 mm, tidak diiris | 123 | °C | ASTM D 648 |
HDT, 1,82 MPa, 6,4 mm, tidak diiris | 133 | °C | ASTM D 648 |
FISIK | Nilai | Satuan | Standar |
Gravitasi Spesifik | 1.2 | - | ASTM D 792 |
Penyerapan air, 24 jam | 0.15 | % | ASTM D 570 |
Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode SABIC |
Tingkat Aliran Peleburan, 300°C/1,2 kgf | 18 | g/10 menit | ASTM D 1238 |
Sumber GMD, terakhir diperbarui:06/18/1999 |
Parameter | ||
Pencetakan Injeksi | Nilai | Satuan |
Suhu Pengeringan | 120 | °C |
Waktu Pengeringan | 3 - 4 | jam |
Waktu pengeringan (kumulatif) | 48 | jam |
Suhu Peleburan | 280 - 305 | °C |
Suhu Cetakan | 70 - 95 | °C |
Sumber GMD, terakhir diperbarui:06/18/1999 |
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
Sabic Lexan 121SRM.pdf |