S-Plastics Colorcomp J1000R resin is a compound based on Polysulfone resin. Added features include : Mold Release
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 89 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 71 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2700 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 128 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 5.9E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 5.8E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 199 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.9 | % | S-Plastics Method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.9 | % | ISO 62-1 |
| Source GMD, last updated:06/05/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 150 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 355 - 370 | °C |
| Front - Zone 3 Temperature | 370 - 380 | °C |
| Middle - Zone 2 Temperature | 360 - 370 | °C |
| Rear - Zone 1 Temperature | 345 - 355 | °C |
| Mold Temperature | 140 - 150 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 60 - 100 | rpm |
| Source GMD, last updated:06/05/2008 | ||
|
For more information please download the datesheet |
|
 |
S-Plastics Colorcomp J1000R.pdf |
|