S-Plastics Stat-kon QD000I resin is a compound based on Nylon 6/10 resin containing Carbon Powder, Impact Modifier. Added features of this
material include: Electrically Conductive, High Impact.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 31 | MPa | ASTM D 638 |
| Tensile Strain, break | 52.7 | % | ASTM D 638 |
| Flexural Stress | 54 | MPa | ASTM D 790 |
| Flexural Modulus | 1720 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 603 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 55 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.17E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.17E-04 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.11 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.28 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.2 - 0.4 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 1 - 3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1 - 3 | % | ISO 294 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+02 - 1.E+04 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | 1.E+02 - 1.E+04 | Ohm | ASTM D 257 |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.12 - 0.2 | % |
| Melt Temperature | 270 - 275 | °C |
| Front - Zone 3 Temperature | 270 - 280 | °C |
| Middle - Zone 2 Temperature | 260 - 270 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||